全自動攪拌車實心輪胎造成損壞的原因！
今天就帶您來了解造成全自動攪拌車實心輪胎損壞的原因，希望能給大家?guī)硪恍椭?
Today, I will take you to understand the causes of solid tire damage of automatic mixer, hoping to bring you some help.
1、脫層，橡膠之間發(fā)生了周向裂口或著是分層。
1. Delamination, circumferential cracking or delamination between rubbers.
造成脫層的原因：
Causes of delamination:
（1）膠料中可能含有水分戶或者是其他雜物，尤其是纖維膠在儲運的過程中被雨水、雜物污染。
(1) Rubber may contain moisture or other debris, especially fiber glue in the process of storage and transportation by rain, debris pollution.
（2）胎胚保溫不良、硫化機的溫度波動造成了欠硫。
(2) The poor heat preservation of the embryo and the temperature fluctuation of the vulcanizer caused the under sulfur.
（3）胎胚成型太早而且停放時間太長，造成了胎胚膠料的自硫。
(3) The formation of embryo is too early and the storage time is too long, resulting in the self sulfur of the compound in the center of embryo.
（4）使用時超載、超速運行。
(4) When in use, it is overloaded and overspeed.
2、脫圈，發(fā)生全自動攪拌車脫圈的原因：
2. The reasons for the ring separation of the full-automatic mixer are as follows:
（1）粘合劑粘度沒有達到工藝要求。
(1) The viscosity of adhesive did not meet the process requirements.
（2）涂粘合劑之后表面受到了污染。
(2) The surface was contaminated after the adhesive was applied.
（3）胎胚保溫不良、硫化機的溫度有波動造成了欠硫。
(3) The poor heat preservation of the embryo and the fluctuation of the temperature of the vulcanizer caused the lack of sulfur.
（4）使用時超載、超速運行。
(4) When in use, it is overloaded and overspeed.
以上就是關于全自動攪拌車實心輪胎造成損壞的原因，希望對大家有所幫助，如想了解更多資訊內(nèi)容請點擊官網(wǎng)：全自動攪拌車廠家http://jbckj.cn。
The above is about the reasons for the damage of the solid tire of the automatic mixer. I hope it can help you. For more information, please click the official website: the manufacturer of the automatic mixer http://jbckj.cn 。